Fabrication of Polymer-Derived Silicon Oxycarbide Microparts and Their Mechanical Characteristics

[+] Author and Article Information
Takahiro Namazu

Associate Professor
Division of Mechanical Systems,
Department of Mechanical and Systems Engineering,
University of Hyogo
2167 Shosha, Himeji,
Hyogo 671-2201, Japan;
JST PRESTO,
Japan Science and Technology Agency,
4-1-8, Honcho, Kawaguchi,
Saitama 332-0012, Japan
e-mail: namazu@eng.u-hyogo.ac.jp

Hiroyuki Kudara

Division of Mechanical Systems,
Department of Mechanical and Systems Engineering,
University of Hyogo,
2167 Shosha, Himeji,
Hyogo 671-2201, Japan

Yoshio Hasegawa

R&D Division,
ART KAGAKU Co., Ltd.,
3135-20, Muramatsu,
Tokai-mura, Naka-gun,
Ibaraki 319-1112, Japan

Contributed by the Manufacturing Engineering Division of ASME for publication in the JOURNAL OF MICRO- AND NANO-MANUFACTURING. Manuscript received March 10, 2014; final manuscript received May 20, 2014; published online July 9, 2014. Assoc. Editor: Nicholas Fang.

J. Micro Nano-Manuf 2(4), 044501 (Jul 09, 2014) (7 pages) Paper No: JMNM-14-1013; doi: 10.1115/1.4027734 History: Received March 10, 2014; Revised May 20, 2014

In this paper, fabrication and mechanical characterization of silicon oxycarbide (SiOC) microparts made from polycarbosilane (PCS) precursor is described. The developed fabrication technique is a combination of ultraviolet thick photoresist lithography and slip casting. The slips consisting of β-SiC nanoparticles and a PCS solution are cast into SU-8 photoresist micromold, fabricated on a porous tungsten carbide plate. The plate works as a filter for solid–liquid separation. The cast slips are fired at 1000 °C in N2 gas flow for an hour. During the firing, the SiOC body can be released from the mold because of SU-8 vaporization at 450 °C. By using the technique, we have successfully produced SiOC microgears with diameters ranging from 0.5 mm to 2 mm. To improve the mechanical reliability, the polymer infiltration and pyrolysis (PIP) process is carried out. The influence of the PIP process is evaluated by means of the nanoindentation test. The Young's modulus and hardness are increased with increasing PIP process cycles. From energy dispersive X-ray measurement results, it is found that their distributions are related to the amount of oxygen and the carbon-to-silicon ratio.

FIGURES IN THIS ARTICLE
<>
Copyright © 2014 by ASME
Your Session has timed out. Please sign back in to continue.

References

Chang, K-S., Tanaka, S., and Esashi, M., 2003, “MEMS-Based Fuel Reformer With Suspended Membrane Structure,” IEEJ Trans. Sens. Micromach., 123(9), pp. 346–350. [CrossRef]
Ehrich, F. F., and Jacobson, S. A., 2003, “Development of High-Speed Gas Bearings for High-Power Density Microdevices,” ASME J. Eng. Gas Turbine Power, 125(1), pp. 141–148. [CrossRef]
Jacobson, S. A., and Epstein, A. H., 2003, “An Informal Survey of Power MEMS,” Proc. ISMME, p. K18.
Mitcheson, P. D., Reilly, E. K., Toh, T., Wright, P. K., and Yeatman, E. M., 2006, “Transduction Mechanisms and Power Density for MEMS Inertial Energy Scavengers,” Power MEMS '06, pp. 275–278.
Kang, P., Tanaka, S., and Esashi, M., 2005, “Demonstration of a MEMS-Based Turbocharger on a Single Rotor,” J. Micromech. Microeng., 15(5), pp. 1076–1087. [CrossRef]
Hanein, Y., Pan, Y. V., Ratner, B. D., Denton, D. D., and Bohringer, K. F., 2001, “Micromachining of Non-Fouling Coatings for Bio-MEMS Applications,” Sens. Actuators, B, 81(1), pp. 49–54. [CrossRef]
Miki, N., Teo, C. J., Ho, L. C., and Zhang, X., 2003, “Enhancement of Rotordynamic Performance of High-Speed Micro-Rotors for Power MEMS Applications by Precision Deep Reactive Ion Etching,” Sens. Actuators, A, 104(3), pp. 263–267. [CrossRef]
Zhang, X., Chen, K.-S., and Spearing, S. M., 2003, “Thermo-Mechanical Behavior of Thick PECVD Oxide Films for Power MEMS Applications,” Sens. Actuators, A, 103(1–2), pp. 263–270. [CrossRef]
Bhardwaj, J., Ashraf, H., and McQuarrie, A., 1997, “Dry Silicon Etching for MEMS,” Symposium on Microstructures and Microfabricated Systems, pp. 4–9.
Petersen, K. E., 1982, “Silicon as a Mechanical Material,” Proc. IEEE, 70(5), pp. 420–457. [CrossRef]
Stoldt, C. R., Carraro, C., Ashurst, W. R., Gao, D., Howe, R. T., and Maboudian, R., 2002, “A Low-Temperature CVD Process for Silicon Carbide MEMS,” Sens. Actuators, A, 97–98(1), pp. 410–415. [CrossRef]
Shah, S. R., and Raj, R., 2002, “Mechanical Properties of a Fully Dense Polymer Derived Ceramic Made by a Novel Pressure Casting Process,” Acta Mater., 50(16), pp. 4093–4103. [CrossRef]
Ishida, Y., Takahashi, T., Okumura, H., Sekigawa, T., and Yoshida, S., 1999, “Elongated Shaped Si Island Formation on 3D-SiC by Chemical Vapor Deposition and Its Application to Antiphase Domain Observation,” Jpn. J. Appl. Phys., 38(6A), pp. 3470–3474. [CrossRef]
Maboudian, R., Carraro, C., Senesky, D. G., and Roper, C., 2013, “Advances in Silicon Carbide Science and Technology at the Micro- and Nanoscales,” J. Vac. Sci. Technol. A, 31(5), p. 050805. [CrossRef]
Senesky, D. G., Jamshidi, B., Cheng, K. B., and Pisano, A. P., 2009, “Harsh Environment Silicon Carbide Sensors for Health and Performance Monitoring of Aerospace Systems: A Review,” IEEE Sens. J., 9(11), pp. 1472–1478. [CrossRef]
Chen, T., Dong, M., Wang, J., Zhang, L., and Li, C., 2012, “Study on Properties of Silicon Oxycarbide Thin Films Prepared by RF Magnetron Sputtering,” 2nd International Conference on Electronic and Mechanical Engineering and Information Technology, EMEIT-2012, pp. 1233–1237.
Strachota, A., Cerný, M., Glogar, P., Sucharda, Z., Havelcová, M., Chlup, Z., Dlouhý, I., and Kozák, V., 2011, “Preparation of Silicon Oxycarbide Composites Toughened by Inorganic Fibers via Pyrolysis of Precursor Siloxane Composites,” Acta Phys. Polon. A, 120(2), pp. 326–330.
Kleebe, H.-J., and Blum, Y. D., 2008, “SiOC Ceramic With High Excess Free Carbon,” J. Eur. Ceram. Soc., 28(5), pp. 1037–1042. [CrossRef]
Toma, L., Kleebe, H.-J., Müller, M. M., Janssen, E., Riedel, R., Melz, T., and Hanselka, H., 2012, “Correlation Between Intrinsic Microstructure and Piezoresistivity in a SiOC Polymer-Derived Ceramic,” J. Am. Ceram. Soc., 95(3), pp. 1056–1061. [CrossRef]
Narisawa, M., Sumimoto, R., and Kita, K., 2010, “Evaluation of Oxidation Resistance of Thin Continuous Silicon Oxycarbide Fiber Derived From Silicone Resin With Low Carbon Content,” J. Mater. Sci., 45, pp. 5642–5648. [CrossRef]
Tanaka, S., Sugimoto, S., Li, J.-F., Watanabe, R., and Esashi, M., 2001, “Silicon Carbide Micro-Reaction-Sintering Using Micromachined Silicon Molds,” J. Microelectromech. Syst., 10(1), pp. 55–61. [CrossRef]
Ishikawa, T., Namazu, T., Yoshiki, K., Inoue, S., and Hasegawa, Y., 2010, “Polycarbosilane-Derived Silicon-Carbide MEMS Component Fabricated by Slip Casting With SU8 Micro Mold,” 23rd IEEE International Conference on Microelectromechanical Systems, MEMS 2010, pp. 416–419.
Namazu, T., Ishikawa, T., and Hasegawa, Y., 2011, “Influence of Polymer Infiltration and Pyrolysis Process on Mechanical Strength of Polycarbosilane-Derived Silicon Carbide Ceramics,” J. Mater. Sci., 46(9), pp. 3046–3051. [CrossRef]
Hasegawa, Y., and Okamura, K., 1983, “Synthesis of Continuous Silicon Carbide Fibre; Part 3 Pyrolysis Process of Polycarbosilane and Structure of the Products,” J. Mater. Sci., 18(12), pp. 3633–3648. [CrossRef]
Soraru, G. D., Babonneau, F., and Mackenzie, J. D., 1990, “Structural Evolutions From Polycarbosilane to SiC Ceramic,” J. Mater. Sci., 25(9), pp. 3886–3893. [CrossRef]
Hasegawa, Y., “New Curing Method for Polycarbosilane With Unsaturated Hydrocarbons and Application to Thermally Stable SiC Fibre,” Compos. Sci. Technol., 51(2), pp. 161–166. [CrossRef]
Narisawa, M., Kado, H., Mori, R., Yoshida, M., Mabuchi, H., Kohyama, A., and Satoh, M., 2007, “Influence of Network Structure on Abnormally High Viscosity of Mixed Slurries of Silicon Carbide Nanopowder and Polycarbosilane,” J. Ceram. Soc. Jpn., 115(12), pp. 982–986. [CrossRef]
Zhu, S., Ding, S., Xi, H., and Wang, R., 2005, “Low-Temperature Fabrication of Porous SiC Ceramics by Preceramic Polymer Reaction Bonding,” Mater. Lett., 59(5), pp. 595–597. [CrossRef]
Jose, M., Ferreira, F., and Diz, H. M. M., 1999, “Effect of Solids Loading on Slip-Casting Performance of Silicon Carbide Slurries,” J. Am. Ceram. Soc., 82(8), pp. 1993–2000.
Sugiyama, K., and Korizuki, N., 1995, “Preparation of Low Density Free-Standing Shape of SiC by Pressure-Pulsed Chemical Vapour Infiltration,” J. Mater. Sci. Lett., 14(23), pp. 1720–1722. [CrossRef]
Mehregany, M., and Zorman, C. A., 1999, “SiC MEMS: Opportunities and Challenges for Applications in Harsh Environments,” Thin Solid Films, 355–356(1), pp. 518–524. [CrossRef]
Sugimoto, M., Shimoo, T., Okamura, K., and Seguchi, T., 1995, “Reaction Mechanisms of Silicon Carbide Fiber Synthesis by Heat Treatment of Polycarbosilane Fibers Cured by Radiation: II, Free Radical Reaction,” J. Am. Ceram. Soc., 78(7), pp. 1849–1852. [CrossRef]
Bouillon, E., Langlais, F., Pailler, R., Naslain, R., Cruege, F., Huong, P. V., Sarthou, J. C., Delpuech, A., Laffon, C., Lagarde, P., Monthioux, M., and Oberlin, A., 1991, “Conversion Mechanisms of a Polycarbosilane Precursor Into an SiOC-Based Ceramic Material,” J. Mater. Sci., 26(5), pp. 1333–1345. [CrossRef]
Mah, T., Hecht, N. L., McCullum, D. E., Hoenigman, J. R., Kim, H. M., Katz, A. P., and Lipsitt, H., 1984, “Thermal Stability of SiC Fibres,” J. Mater. Sci., 19(4), pp. 1191–1201. [CrossRef]
Simon, G., and Bunsell, A. R., 1984, “Creep Behaviour and Structural Characterization at High Temperatures of Nicalon SiC Fibres,” J. Mater. Sci., 19(11), pp. 3658–3670. [CrossRef]
Sasaki, Y., and Nishina, Y., 1987, “Raman Study of SiC Fibres Made From Polycarbosilane,” J. Mater. Sci., 22, pp. 443–448. [CrossRef]
Hemida, A. T., Pailler, R., and Naslain, R., 1997, “Continuous SiC-Based Model Monofilaments With a Low Free Carbon Content: Part I: From the Pyrolysis of a Polycarbosilane Precursor Under an Atmosphere of Hydrogen,” J. Mater. Sci., 32(9), pp. 2359–2366. [CrossRef]
Okamura, K., 1987, “Ceramic Fibres From Polymer Precursors,” Composites, 18(2), pp. 107–120. [CrossRef]
Zawrah, M. F., and El-Gazery, M., 2007, “Mechanical Properties of SiC Ceramics by Ultrasonic Nondestructive Technique and Its Bioactivity,” Mater. Chem. Phys., 106(2–3), pp. 330–337. [CrossRef]

Figures

Grahic Jump Location
Fig. 1

A schematic of fabrication process for PCS-derived SiOC micromechanical parts. The combination of UV thick resist photolithography and slip casting is named microslip casting. First SU-8 sheet is laminated onto a WC plate. Then, photolithography, baking, and development are conducted to fabricate SU-8 micromold with gear pattern. After that, the slips are cast into the mold. During casting, we apply a pressure and a depressure over and under the mold, respectively, for smooth solid–liquid separation. To make the cast body denser, the casting and pressuring–depressuring process is repeated several times. After casting, the cast body is fired. During firing, the mold is evaporated. By applying a small shear force to SiOC gears, they can be easily released.

Grahic Jump Location
Fig. 2

Photographs of the polished and blasted WC plates along with their magnified pictures. These were used as a filter for solid–liquid separation. The blasted plate is better for the fabrication of crack-less SiOC parts because lots of pores are distributed more uniformly on the surface.

Grahic Jump Location
Fig. 3

Examples of microgear mold made of SU-8 photoresist. When applying the best lithography condition for SU-8 on Si wafer to SU-8 on WC plate, a gear pattern could not be finely made. When the best condition for SU-8 on the plate was found, finely shaped gear mold could be realized.

Grahic Jump Location
Fig. 4

Photographs of the topside and backside of SiOC microgears fabricated through the CPD process of 2, 3, and 6 cycles. In total the amount of the slips used per one fabrication was 600 μl, which was maintained for all the fabrications. When the CPD process cycles were twice, which indicates that the slips of 300 μl were cast twice, many lost cogs and cracks were found. With increasing the cycles, these were reduced. At 6 cycles, no lost cogs were found. Multiple CPD process cycles are effective for finely shaped SiOC parts.

Grahic Jump Location
Fig. 5

Photograph of fabricated several types of SiOC microgears after 6 times casting processes. Even gears with the diameter less than 1 mm could be finely made. The diameter of the smallest gear is approximately 300 μm.

Grahic Jump Location
Fig. 6

Photographs of the backside of SiOC microgears after 6, 9, and 12 PIP cycles. With increasing PIP cycles, a dark-colored portion appears to increase. This indicates that the gear is getting denser by conducting multiple PIP cycles.

Grahic Jump Location
Fig. 7

Relationship between the number of PIP cycles and the density of SiOC. No large differences between polished and blasted WC plates are seen.

Grahic Jump Location
Fig. 8

Process flow for fabricating the specimen for the nanoindentation test. A groove with the width and depth of 250 μm and 200 μm, respectively, was fabricated using a dicing cutter onto 300 μm-thick diced silicon chip. Epoxy glue was applied onto the silicon chip, and then half-cut SiOC gear was put onto the groove for bonding. At the same time, two silicon blocks were also bonded for the support of the gear. The cut face was investigated by the nanoindentation test.

Grahic Jump Location
Fig. 9

Nanoindentation-derived hardness and Young's modulus maps on SiOC surfaces after 6, 9, and 12 PIP cycles along with O and C/Si maps derived from EDX. Darker portion in each map is indicative of higher portion in each parameter. It is found that higher Young's modulus and hardness were obtained where less O content and the C/Si ratio closer to 1.

Grahic Jump Location
Fig. 10

Relationships between O content, C/Si content ratio, and SiOC Young's modulus. With increasing PIP cycles, O content was reduced and C/Si ratio was getting close to 1. As the result an increase of the Young's modulus was provided.

Tables

Errata

Discussions

Some tools below are only available to our subscribers or users with an online account.

Related Content

Customize your page view by dragging and repositioning the boxes below.

Related Journal Articles
Related eBook Content
Topic Collections

Sorry! You do not have access to this content. For assistance or to subscribe, please contact us:

  • TELEPHONE: 1-800-843-2763 (Toll-free in the USA)
  • EMAIL: asmedigitalcollection@asme.org
Sign In