A model is developed herein for predicting the evolution of interface degradation, matrix cracking, and delamination at multiple sites in laminated continuous fiber composite plates subjected to monotonic and/or cyclic mechanical loading. Due to the complicated nature of the many cracks and their interactions, a multi-scale micro-meso-local-global methodology is deployed in order to model all damage modes. Interface degradation is first modeled analytically on the microscale, and the results are homogenized to produce a cohesive zone model that is capable of predicting interface fracture. Subsequently, matrix cracking in the plies is modeled analytically on the meso-scale, and this result is homogenized to produce ply level damage dependent constitutive equations. The evolution of delaminations is considered on the local scale, and this effect is modeled using a three dimensional finite element algorithm. Results of this analysis are homogenized to produce damage dependent laminate equations. Finally, global response of the damaged plate is modeled using a plate finite element algorithm. Evolution of all three modes of damage is predicted via interfacing all four scales into a single multi-scale algorithm that is computationally tenable for use on a desktop computer. Results obtained herein suggest that this model may be capable of accurately predicting complex damage patterns such as that observed at open holes in laminated plates.

1.
Talreja
R.
, “
Transverse Cracking and Stiffness Reduction in Composite Laminates
,”
Journal of Composite Materials
, Vol.
19
, pp.
355
375
,
1985
.
2.
Lee
J.-W.
,
Allen
D. H.
, and
Harris
C. E.
, “
Internal State Variable Approach for Predicting Stiffness Reduction in Fibrous Laminated Composites with Matrix Cracks
,”
Journal of Composite Materials
, Vol.
23
, pp.
1273
1291
,
1989
.
3.
Lim
S. G.
, and
Hong
C. S.
, “
Prediction of Transverse Cracking and Stiffness Reduction in Cross-Ply Laminated Composites
,”
Journal of Composite Materials
, Vol.
23
, pp.
695
713
,
1989
.
4.
Highsmith, A. L., and K. L. Reifsnider, “Stiffness-Reduction Mechanisms in Composite Laminates,” Damage in Composite Materials, ASTM STP 775, L. L. Reifsnider, ed., American Society for Testing and Materials, pp. 103–117, 1982.
5.
Laws
N.
,
Dvorak
G. J.
, and
Hejazi
M.
, “
Stiffness Changes in Unidirectional Composites Caused by Crack Systems
,”
Mechanics of Materials
, Vol.
2
, pp.
123
137
,
1983
.
6.
Laws, H., and G. J. Dvorak, “The Loss of Stiffness of Cracked Laminates,” Proceedings IUTAM Eshelby Memorial Symposium. London, Cambridge University Press, p. 19, 1985.
7.
Dvorak, G. J., “Analysis of Progressive Matrix Cracking in Composite Laminates,” AFOSR-82-0308, Rensselaer Polytechnic Institute, 1985.
8.
Mura, T., “Micromechanics of Defects in Solids,” Mechanics of Elastic and Inelastic Solids 3, Martinus Nijhoff Publishers, Printed in the Netherlands, 1982.
9.
Hill
R.
, “
A Self-Consistent Mechanics of Composite Materials
,”
Journal of the Mechanics and Physics of Solids
, Vol.
13
, pp.
213
222
,
1965
.
10.
Hashin
Z.
, “
Analysis of Cracked Laminates: A Variational Approach
,”
Mechanics of Materials
, Vol.
4
, pp.
121
136
,
1985
.
11.
Aboudi
J.
, “
Stiffness Reduction of Cracked Solids
,”
Engineering Fracture Mechanics
, Vol.
26
, pp.
637
650
,
1987
.
12.
Talreja, R., “A Continuum Mechanics Characterization of Damage in Composite Materials,” Proceedings Royal Society of London, Vol. 399, 1985.
13.
Talreja
R.
, “
Stiffness Properties of Composite Laminates with Matrix Cracking and Interior Delamination
,”
Engineering Fracture Mechanics
, Vol.
25
, pp.
751
762
,
1986
.
14.
Allen
D. H.
,
Harris
C. E.
, and
Groves
S. E.
, “
A Thermomechanical Constitutive Theory for Elastic Composites with Distributed Damage—Part I: Theoretical Development
,”
International Journal of Solids and Structures
, Vol.
23
, pp.
1301
1318
,
1987
.
15.
Allen
D. H.
,
Harris
C. E.
, and
Groves
S. E.
, “
A Thermomechanical Constitutive Theory for Elastic Composites with Distributed Damage—Part II: Application to Matrix Cracking in Laminated Composites
,”
International Journal of Solids and Structures
, Vol.
23
, pp.
1319
1338
,
1987
.
16.
Kachanov
M.
, “
Continuum Theory of Media with Cracks
,”
Izv. AN SSR, Mekhanika Tverdogo Tela, ASCE
, Vol.
7
, pp.
54
59
,
1972
.
17.
Harris
C. E.
,
Allen
D. H.
,
Nottorf
E. W.
, and
Groves
S. E.
, “
Modeling Stiffness Loss in Quasi-Isotropic Laminates Due to Microstructural Damage
,”
ASME JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY
, Vol.
110
, pp.
128
133
,
1988
.
18.
Allen, D. H., S. E. Groves, and C. E. Harris, “A Cumulative Damage Model for Continuous Fiber Composite Laminates with Matrix Cracking and Interply Delaminations,” ASTM STP for 8th Symposium on Composite Materials: Testing and Design, American Society for Testing and Materials, 1987.
19.
Allen, D. H., Nottorf, E. W., and Harris, C. E., “Effect of Microstructural Damage on Ply Stresses in Laminated Composites,” Recent Advances in the Macro- and Micro- Mechanics of Composite Materials Structures, D. Hui and J. R. Vinson, eds., American Society of Mechanical Engineers, Chicago, AD-Vol. 13, pp. 135–146, 1988.
20.
Yoon, C., and Allen, D. H., “Damage Dependent Constitutive Behavior and Energy Release Rate for a Cohesive Zone in a Thermoviscoelastic Solid,” to appear in International Journal of Fracture, 1999.
21.
Allen, D. H., and Searcy, C. R., “A Micromechanical Model for a Viscoelastic Cohesive Zone,” submitted to International Journal of Fracture, 1998.
22.
Boyd
J. G.
,
Costanzo
F.
, and
Allen
D. H.
, “
A Micromechanics Approach for Constructing Locally Averaged Damage Dependent Constitutive Equations in Inelastic Composites
,”
International Journal of Damage Mechanics
, Vol.
2
, pp.
209
228
,
1993
.
23.
Allen
D. H.
, and
Yoon
C.
, “
Homogenization Techniques for Thermoviscoelastic Solids Containing Cracks
,”
International Journal of Solids and Structures
, Vol.
35
, pp.
4035
4054
,
1998
.
24.
Allen, D. H., and Searcy, C. R., “Numerical Aspects of a Micromechanical Model of a Cohesive Zone,” to appear in Journal of Reinforced Plastics and Composites, 1999.
25.
Foulk, J. W., Allen, D. H., and Helms, K. L. E., “Formulation of a Three Dimensional Cohesive Zone Model for Application to a Finite Element Algorithm,” to appear in Computational Methods in Applied Mechanics and Engineering, 1999.
26.
Lee, J. W., Allen, D. H., and Harris, C. E., “The Upper Bounds of Reduced Axial and Shear Moduli in Cross-Ply Laminates with Matrix Cracks,” Composite Materials: Fatigue and Fracture (Third Volume), ASTM STP 1110, T. K. O’Brien, ed., American Society for Testing and Materials, Philadelphia, pp. 56–69, 1991.
27.
Lee
J. W.
,
Allen
D. H.
, and
Harris
C. E.
, “
The Upper Bonds of Reduced Axial and Shear Moduli in Crossply Laminates With Matrix Cracks
,”
Composite Materials: Fatigue and Fracture
, Vol.
3
, pp.
56
69
,
1991
.
28.
Lee, J.-W., “An Analytical Prediction of Matrix Cracking in Fibrous Composite Laminates,” Ph.D. thesis, Texas A&M University, December 1990.
29.
Allen
D. H.
,
Harris
C. E.
,
Groves
S. E.
, and
Norvell
R. G.
, “
Characterization of Stiffness Loss in Crossply Laminates With Curved Matrix Cracks
,”
J. Composites and Materials
, Vol.
22
, pp.
71
80
,
1988
.
30.
Allen, D. H., Groves, S. E., and Harris, C. E., “A Cumulative Damage Model for Continuous Fiber Composite Laminates with Matrix Cracking and Interply Delaminations,” Composite Materials: Testing and Design (8th Conference), ASTM STP 972, J. D. Whitcomb, Ed., American Society for Testing and Materials, Philadelphia, pp. 57–79, 1988.
31.
Allen, D. H., “Damage Evolution in Laminates,” Damage Mechanics of Composite Materials, R. Talreja, ed., Composite Materials, Series, R. B. Pipes, Series, ed., Martinus-Nijhoff, pp. 79–116, 1994.
32.
Buie, K. D., “A Finite Element Model for Laminated Composite Plates With Matrix Cracks and Delaminations,” M. S. thesis, Texas A&M University, 1988.
This content is only available via PDF.
You do not currently have access to this content.