A Criterion to predict under what conditions EAC would initiate in cracks in a high-sulfur steel in contact with low-oxygen water was recently proposed by Wire and Li (1996). This EAC initiation criterion was developed using transient analyses for the diffusion of sulfides plus experimental test results. The experiments were conducted mainly on compact tension-type specimens with initial crack depths of about 2.54mm. The present paper expands upon the work of Wire and Li by presenting results for significantly deeper initial semi-elliptical surface cracks. In addition, in one specimen, the surface crack penetrated weld-deposited cladding into the high-sulfur steel. The results for the semi-elliptical surface cracks agreed quite well with the EAC initiation criterion, and provide confirmation of the applicability of the criterion to crack configurations with more restricted access to water.
Skip Nav Destination
Article navigation
Research Papers
The Initiation of Environmentally Assisted Cracking in Semi-Elliptical Surface Cracks
L. A. James
L. A. James
Bettis Atomic Power Laboratory, Westinghouse Electric Corporation, P.O. Box 79, West Mifflin, PA 15122-0079
Search for other works by this author on:
L. A. James
Bettis Atomic Power Laboratory, Westinghouse Electric Corporation, P.O. Box 79, West Mifflin, PA 15122-0079
J. Pressure Vessel Technol. May 1998, 120(2): 200-206 (7 pages)
Published Online: May 1, 1998
Article history
Received:
November 14, 1997
Revised:
December 5, 1997
Online:
February 11, 2008
Citation
James, L. A. (May 1, 1998). "The Initiation of Environmentally Assisted Cracking in Semi-Elliptical Surface Cracks." ASME. J. Pressure Vessel Technol. May 1998; 120(2): 200–206. https://doi.org/10.1115/1.2842241
Download citation file:
16
Views
Get Email Alerts
Cited By
Related Articles
Corrosion Fatigue Crack Growth in Clad Low-Alloy Steels—Part I: Medium-Sulfur Forging Steel
J. Pressure Vessel Technol (August,1997)
Corrosion Fatigue Crack Growth in Clad Low-Alloy Steels—Part II: Water Flow Rate Effects in High-Sulfur Plate Steel
J. Pressure Vessel Technol (August,1997)
The Effect of Water Flow Rate Upon the Environmentally Assisted
Cracking Response of a Low-Alloy Steel
J. Pressure Vessel Technol (August,1995)
Experimental Study on Crack Growth Behavior for Austenitic Stainless Steel in High Temperature Pure Water
J. Pressure Vessel Technol (May,1986)
Related Proceedings Papers
Related Chapters
Radial Delayed Hydride Cracking in Irradiated Zircaloy-2 Cladding: Advanced Characterization Techniques
Zirconium in the Nuclear Industry: 20th International Symposium
A 3D Cohesive Modelling Approach for Hydrogen Embrittlement in Welded Joints of X70 Pipeline Steel
International Hydrogen Conference (IHC 2012): Hydrogen-Materials Interactions
Introduction and Definitions
Handbook on Stiffness & Damping in Mechanical Design